Performance and Microstructure of Ultra Low Ion Permeability Cementitious Materials
WANG Xin gang,SONG Gu quan,CHEN Li he and ZHANG Ai ping
DOI:10.11835/j.issn.1674-4764.2009.05.026
Received February 18, 2009,Revised , Accepted , Available online July 01, 2015
Volume ,2009,Pages 138-144
- Abstract
Microstructure and macro performance of Ultra Low Ion Permeability Cementitious Materials (ULIPCM) were investigated by Micro hardness, MIP and SEM EDXA. It was shown that the compressive strength of ULIPCM was more than 80 MPa, flexural strength was more than 11.0 MPa, and elastic modulus was in the range of 38.0 to 42.0 GPa at the age of 28 days; chloride diffusion coefficient was lower than 0.8×10－13m2·s－1, conductive charge for 6 hours was lower than 300 coulombs; sulfate attack resistance was good; shrinkage at the age of 28 days was lower than 400×10－6. Compared with ordinary concrete with which thickness of interfacial transition zone is 60 to 100 μm, the thickness of interfacial transition zone of ULIPCM was lower than 30 μm. Penetration paths of corrosive medium were effectively interrupted in ULIPCM. And pore structure parameters, such as porosity and the most probable pore radius of ULIPCM, were also obviously optimized in ULIPCM. Besides, few CH crystals were in the ULIPCM aggregate and the interfacial transition zone of ULIPCM. And the orientation of CH crystals was poor.